Scott, you are quite correct.  I have bought both polyester and epoxy and it was the polyester that I used (sorry about the confusion)....which may account for the poor bond with the aluminium.  I still did not get a good result overall which I suspect is due to the varying temperatures during curing.   I will sort out some form of temperature control and give it another go.

Thanks for the feedback.