Hi Gary

The first thing I'd check on yours is that the belt is tensioned correctly. It's easily adjusted and could potentially struggle to start if it's too tight. Left like that it could overload and burn out the motor. If the tension is ok the make sure nothing is jamming the belt or rollers, the machine should be occasionally oiled and cleaned in any case just like any other.


You can get a sharp edge quite easily with a 120g belt. Same as I use but also 240g and even though I have higher grits I rarely use them unless I want a polished edge. Lower grits as advised are useful for re profiling a tool and make sure you have a tub of water and cloth handy for cooling.


I can't understand why you can't get an edge unless you just aren't grinding far enough and you certainly should have no need to apply excess pressure which will cause the tool to overheat and overwork the motor.


I'm just north of Morpeth and quite happy to have a look at your pro edge or show you how I use mine. If you want to take me up on that just send me a pm.

Bob


Message to the OP

I've had the lot. including a Tormek and for turning tools it's the only machine I now use. I also use it for many other things and as far as I'm concerned it's worth the money even though I think it and the Axminster clones are overpriced. I don't sharpen my bench chisels on it though prefering to use diamond plates.